Heraenium® CE
The classical partial denture alloy with optimal strength and elasticity, and years of clinical testing.
Benefits
- Excellent strength and elasticity
- Exceptional flowability and mould filling capability
Specifications
| Product details | ||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
|
Composition (content in mass %) |
Co 63.5 Cr 27.8 Mo 6.6 Mn 0.6 Si 1.0 C 0.3 N 0.2 |
|||||||||||||
| Type | 5 (s) | |||||||||||||
| Shade | Grey | |||||||||||||
| Indication | 6 | |||||||||||||
| Article code | ||||||||||||||
| Technical data, melting and casting | ||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Melting range |
Solidus 1330 °C Liquidus 1380 °C |
|||||||||||||
| Preheating Temperature | 950 – 1050 °C | |||||||||||||
| Casting Temperature | 1530 °C | |||||||||||||
| Crucible | Ceramic NPM | |||||||||||||
| Density | 8.0 g/cm3 | |||||||||||||
| Hardness (HV5) | -- (w/k), -- (v), 380 HV 10 (s) | |||||||||||||
| 0.2 % yield strength (MPa) | -- (w/k), 580(v) | |||||||||||||
| Elongation (%) | -- (w/k), 4(v) | |||||||||||||
| Young's modulus of elasticity (GPa) | 228 | |||||||||||||
| Ceramic firing | ||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| CTE | -- | |||||||||||||
| Oxide firing | -- | |||||||||||||
| Soft annealing | -- | |||||||||||||
| Hardening | -- | |||||||||||||
| Solder / Laser welding wire | ||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Solder |
soldered to Precious metal / Stahlgold Lot 750 soldered to Non-Precious metal / Stahlgold Lot 910 |
|||||||||||||
| Laser welding wire | suitable dental NiCr laser welding wires according to EN ISO 28319 | |||||||||||||